A new test design from the University of Central Florida has challenged modules with different cell technologies. The results show advantages for the heterojunction modules tested. Here we discuss the new method with its designer.
pv magazine: You developed a more realistic test sequence for mechanical load testing which simulates snow, then vibrations caused by wind, then daily temperature variation, then vibrations again. How do you implement this and what is difference to the standard tests included in the IEC [International Electrotechnical Commission] certification?
Eric Schneller, research scientist at the Florida Solar Energy Center institute of the University of Central Florida: The standard IEC sequence that aims to capture cell cracking involves cyclic mechanical loading followed by 50 thermal cycles and 10 humidity freeze cycles. We have implemented a modified sequence that uses this existing test sequence as the core, adding one step before and one step after. To start we use a large, front-side, static mechanical load to create cell cracks. The existing sequence then works to open up these cracks. Finally, an additional cyclic mechanical load is used to stress the cells after thermal exposure.
Why is the “simple” mechanical load test not sufficient?
The existing standard provides a reasonable minimum threshold of quality throughout the industry, but it remains unknown if this test adequately qualifies modules for the full 25-year operational lifetime that is expected. As with many of the other legs in the IEC 61215 standard, we believe there is an opportunity for a modified version that requires modules to withstand more severe testing conditions. Over the course of 25 years, modules are exposed to a wide range of thermal and mechanical stressors and we believe this modified sequence gets us closer to ensuring performance for the full operational lifetime. At the very least this sequence would be a valuable assessment for modules in locations where large mechanical loads are anticipated, such as large snow or wind loads.
Do you see more module failures when using your modified sequence?
In recent years it has become uncommon for typical module constructions to fail the existing mechanical durability testing sequence. This is certainly a positive trend for the industry, demonstrating overall improvement in module design and manufacturing processes. By adding additional steps to the qualification testing, there are certainly some modules that will fall below the 5% performance degradation threshold. As long as the qualification testing is reasonable and realistic, we think it is important to continue to push the industry to exceed prior benchmarks. Ultimately this will extend operational lifetimes of modules and continue to reduce the cost of solar energy.
pv magazine webinar
An improved quality control test, designed by research scientists of the University of Central Florida is simulating environmental stress conditions more realistically. It focuses on snow loads and vibration induced by winds. It induces cracks at the beginning of the test and works to open them up over an assumed lifetime of more than 20 years. A first study unveiled surprising results and demonstrated how different module technologies behave. Eric Schneller, a research scientist at the University of Central Florida, compared individual modules comprising mono and multi PERC (passivated emitter rear contact), mono PERT (passivated emitter rear totally diffused) and HIT (heterojunction with intrinsic thin layer) technologies. Schneller discovered HIT modules from Japanese manufacturer Panasonic performed most favorably compared with the other three modules tested. More details on the test and results will be discussed in the forthcoming pv magazine webinar at 3pm tomorrow (CEST, Berlin). Click here for more information and registration.
You investigated four module technologies and observed a clear trend as to which behaved better. Is this coincidental, due to the quality of the samples used, or do these results exhibit basic characteristics of the technologies? Do you have a theory about why you see these differences, and can you give us a clue?
In this work we investigated a few different module technologies and observed a wide range of responses to our modified testing sequence. It is certainly true that there is some random nature to cell cracking but it is clear from our results that the cell design, cell interconnection technology and packaging materials are critical in the overall mechanical durability of the modules. Cell and module manufacturing processes play an important role in initial crack susceptibility while the packaging and interconnection scheme are important to prevent crack opening or additional crack creation after thermal exposure.
Lắp đặt điện mặt trời Khải Minh Tech
https://ift.tt/2X7bF6x
0906633505
info.khaiminhtech@gmail.com
80/39 Trần Quang Diệu, Phường 14, Quận 3
Lắp đặt điện mặt trời Khải Minh Tech
https://ift.tt/2ZH4TRU
Không có nhận xét nào:
Đăng nhận xét